1100

1100
Product Details

Density2.71 g/cm3 (169 lb/ft3)

Elastic (Young's, Tensile) Modulus69 GPa (10 x 106 psi)

Electrical Conductivity58 % IACS

Elongation at Break5 %

Melting Onset (Solidus)643 °C (1190 °F)

Shear Modulus26 GPa (3.8 106 psi)

Specific Heat Capacity900 J/kg-K

Strength to Weight Ratio55 kN-m/kg

Tensile Strength: Ultimate (UTS)150 MPa (22 x 103 psi)

Tensile Strength: Yield (Proof)140 MPa (20 x 103 psi)

Thermal Conductivity220 W/m-K

Thermal Diffusivity90

Thermal Expansion23.6 µm/m-K