2024-T651

2024-T651
Product Details

Density                       2.77 g/cm3 (173 lb/ft3)

Elastic (Young's, Tensile) Modulus   73 GPa (11 x 106 psi)

Electrical Conductivity                     30 % IACS

Elongation at Break                             5 %

Melting Onset (Solidus)               502 °C (940 °F)

Shear Modulus                  28 GPa (4.1 106 psi)

Specific Heat Capacity                     870 J/kg-K

Definition of Specific Heat Capacity 

Strength to Weight Ratio                 173 kN-m/kg

Tensile Strength: Ultimate (UTS)       480 MPa (70 x 103 psi)

Tensile Strength: Yield (Proof)        360 MPa (52 x 103 psi)

Thermal Conductivity                     120 W/m-K

Thermal Diffusivity                        50

Thermal Expansion                      22.8 µm/m-K

Alloy Composition

Aluminum (Al)                       90.8 to 94.7 %

Copper (Cu)                           3.8 to 4.9 %

Magnesium (Mg)                       1.2 to 1.8 %

Manganese (Mn)                       0.3 to 0.9 %

Iron (Fe)                                0 to 0.5 %

Silicon (Si)                               0 to 0.5 %

Zinc (Zn)                               0 to 0.25 %

Zirconium (Zr)                            0 to 0.2 %

Residuals                               0 to 0.15 %

Titanium (Ti)                            0 to 0.15 %

Chromium (Cr)                            0 to 0.1 %