5052-H112

5052-H112
Product Details

Density2.68 g/cm3 (167 lb/ft3)

Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi)

Electrical Conductivity35 % IACS

Elongation at Break17 %

Melting Onset (Solidus)607 °C (1120 °F)

Shear Modulus26 GPa (3.8 106 psi)

Specific Heat Capacity900 J/kg-K

Specific Heat Capacity900 J/kg-K

Strength to Weight Ratio75 kN-m/kg

Tensile Strength: Ultimate (UTS)200 MPa (29 x 103 psi)

Tensile Strength: Yield (Proof)100 MPa (15 x 103 psi)

Thermal Conductivity140 W/m-K

Thermal Diffusivity58

Thermal Expansion23.8 µm/m-K