5083-H112

5083-H112
Product Details

Density2.66 g/cm3 (166 lb/ft3)

Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi)

Electrical Conductivity29 % IACS

Elongation at Break16 %

Melting Onset (Solidus)574 °C (1070 °F)

Shear Modulus27 GPa (3.9 106 psi)

Specific Heat Capacity900 J/kg-K

Strength to Weight Ratio113 kN-m/kg

Tensile Strength: Ultimate (UTS)300 MPa (44 x 103 psi)

Tensile Strength: Yield (Proof)140 MPa (20 x 103 psi)

Thermal Conductivity120 W/m-K

Thermal Diffusivity50

Thermal Expansion23.9 µm/m-K